Shougang høyere styrke stål for magnetiske anvendelser i motorer

Høyfast stål for magnetiske applikasjoner i motorer 25Swys500 35Swys500 35Swys600 35Swys900 50Swys650 65Swys600

Seriekarakterer

0,25 mm

25SWYS500

0,35 mm

35SWYS500 / 35SWYS600 / 35SWYS900

0,50 mm

50SWYS650

0,65 mm

65SWYS600
Høyfast stål for magnetiske applikasjoner i motorer 25Swys500 35Swys500 35Swys600 35Swys900 50Swys650 65Swys600

Trekk

Søknad

New energy vehicle high-speed drive motor rotor.

Produkt fordeler

The yield strength reaches 950MPa, which is 150MPa higher than the highest yield strength of electrical steel in the world.

Søknad effekt

By using Shougang 35SWYS900 non-oriented electrical steel products, the motor torque increased by 11.3% and the maximum efficiency point increased by 0.7%.

Magnetiske egenskaper og mekaniske egenskaper

Grades Core loss
P1.0/400(W/kg)
Magnetic induction
B50(T)
Hardness
(HV1)
Yield strength
(MPa)
Tensile strength
(MPa)
35SWYS600 38.0 1.63 235 615 685
35SWYS900 60.0 1.54 300 940 960
Høyfast stål for magnetiske applikasjoner i motorer 25Swys500 35Swys500 35Swys600 35Swys900 50Swys650 65Swys600
Høyfast stål for magnetiske applikasjoner i motorer 25Swys500 35Swys500 35Swys600 35Swys900 50Swys650 65Swys600

Silisiumstålmaterialer på lager

Høyfast stål for magnetiske applikasjoner i motorer 25Swys500 35Swys500 35Swys600 35Swys900 50Swys650 65Swys600

Spot engros og detaljhandel

Produksjon Rotor og stator Stacks Core